STUDY OF IRRADIATION INDUCED DEFECTS AND PHASE INSTABILITY IN ? PHASE OF ZR EXCEL ALLOY WITH IN-SITU HEAVY ION IRRADIATION
39th Annual CNS-CNA Student Conference - 2015 June 01
H. Yu (Queen’s University)
Z. Yao (Queen’s University)
M. A. Kirk (Queen’s University)
M. R. Daymond (Queen’s University)
In situ heavy ion irradiation with 1 MeV Kr2+ was carried out to study irradiation induced phase change and atomic lattice defects in theβ phase of Zr Excel alloy. No decomposition of β-Zr was observed under irradiation at either 200 °C or 450 °C. However, ω-Zr particles experienced shape change and shrinkage associated enrichment of Fe in the β/ω interface at 200 °C irradiation but not at 450 °C. The defectevolution in the β-phase was examined with single phase Zr-20Nballoy. It was found that dislocation loops with Burgers vector ½<111> and <001> both present in β-Zr under room temperature irradiation.
Individual Conference-Paper Copies (Electronic Where Available):
- For CNS members, the first 5 copies per calendar year are free, and additional copies are $10 each.
- For non-members, the price is $25 for the first Conference-paper copy in a request, and $10 each for additional copies of papers in the same conference and in the same request.
- Contact the CNS office to order reprints.